Particle size analysis — Small angle X-ray scattering (SAXS)

This document specifies a method for the application of small-angle X-ray scattering (SAXS) to the estimation of mean particle sizes in the 1 nm to 100 nm size range. It is applicable in dilute dispersions where the interaction and scattering effects between the particles are negligible. This document describes several data evaluation methods: the Guinier approximation, model-based data fitting, Monte-Carlo?based data fitting, the indirect Fourier transform method and the expectation maximization method. The most appropriate evaluation method is intended to be selected by the analyst and stated clearly in the report. While the Guinier approximation only provides an estimate for the mean particle diameter, the other methods also give insight in the particle size distribution.

Analyse granulométrique — Diffusion des rayons X aux petits angles (SAXS)

General Information

Status
Published
Publication Date
04-Oct-2020
Current Stage
6060 - International Standard published
Start Date
05-Oct-2020
Due Date
31-May-2020
Completion Date
05-Oct-2020
Ref Project

Relations

Buy Standard

Standard
ISO 17867:2020 - Particle size analysis -- Small angle X-ray scattering (SAXS)
English language
27 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 17867
Second edition
2020-10
Particle size analysis — Small angle
X-ray scattering (SAXS)
Analyse granulométrique — Diffusion des rayons X aux petits
angles (SAXS)
Reference number
ISO 17867:2020(E)
©
ISO 2020

---------------------- Page: 1 ----------------------
ISO 17867:2020(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2020
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2020 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 17867:2020(E)

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Symbols . 2
5 Principle of the method . 2
6 Apparatus and procedure . 3
7 Preliminary procedures and instrument set-up . 6
8 Sample preparation . 6
9 Measurement procedure . 7
10 Data correction procedures . 8
11 Calculation of the mean particle diameter . 9
11.1 General . 9
11.2 Guinier approximation . 9
11.3 Model fitting .10
12 Size distribution determination .10
12.1 Limitations of size distribution determination from SAXS data .10
12.2 A brief overview of methods .11
12.3 Goodness of fit: evaluating fits .11
12.4 Model-based data fitting .11
12.5 Monte Carlo-based data fitting .12
12.6 Indirect Fourier transform (IFT) method .13
12.7 Expectation maximization (EM) method .13
13 Repeatability .14
14 Documentation and test report.14
14.1 Test report .14
14.2 Technical records .14
Annex A (informative) General principle .16
Annex B (informative) System qualification .24
Bibliography .25
© ISO 2020 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 17867:2020(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee ISO/TC 24, Particle characterization including
sieving, Subcommittee SC 4, Particle characterization.
This second edition cancels and replaces the first edition (ISO 17867:2015), which has been technically
revised. The main changes compared to the previous edition are as follows:
— inclusion of various methods for the extraction of particle size distribution by using the SAXS method;
— correction of technical terms.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2020 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 17867:2020(E)

Introduction
This document deals with small-angle X-ray scattering (SAXS), which is performed for particle
size analysis in the 1 nm to 100 nm size range. Under certain conditions (narrow size distributions,
appropriate instrumental configuration, and idealised shape) the limit of 100 nm can be significantly
extended. In ideal circumstances, SAXS can determine the mean particle diameter and particle size
distribution, surface area, and sometimes particle shape in a reasonably rapid measurement time. User-
friendly commercial instruments are available worldwide from a number of manufacturers for both
routine and more sophisticated analyses, and state-of-the-art research instruments are available at
synchrotron radiation facilities.
As in all particle size measurement techniques, care is required in all aspects of the use of the instrument,
collection of data, and further interpretation. Therefore, there is a need for an International Standard
that allows users to obtain good interlaboratory agreement on the accuracy and reproducibility of the
technique.
SAXS can be applied to any hetero-phase system, in which the two or more phases have a different
electron density. In most cases, the electron density corresponds reasonably well to the mass density.
SAXS is sensitive to the squared electron density difference. For fixed volume fractions, it does not
matter whether the particles constitute the denser phase and the solvent (or matrix) is the less-dense
phase or vice versa. Thus, pore size distributions can be measured with SAXS in the same way as size
distributions of oil droplets in emulsions or solid particles in suspensions. Core-shell-nanoparticles can
also be investigated, but low density (e.g. organic) shells are not detected if the core has a significantly
higher density. To obtain the outer particle diameter including the shell, other methods should be used.
Although SAXS allows the determination of particle size, size distribution, surface area, and sometimes
particle shape in concentrated solutions, in powders and in bulk materials, this document is limited
to the description of particle sizes in dilute systems. A dilute system in the sense of SAXS means
that particle interactions are absent. In case of long-range interactions (Coulomb forces between the
particles), special care needs to be taken and a reduction of the concentration or the addition of salt can
be necessary.
Since all illuminated particles present in the X-ray beam are measured simultaneously, SAXS results are
ensemble and time averaged across all the particle orientations which are present in the sample.
The shape of the particles can be assigned to a basic geometry: spheroid, disk, or cylinder. This does not
exclude more detailed information about the shape of the particle being obtained. However, the method
of calculation for more detailed shape analysis is very complex to be included in an International
Standard at this time. The sizes of irregularly shaped nanoparticles can be assessed by the radius of
gyration (R ) as obtained by classic Guinier analysis.
g
The size and size distribution of particles with basic shapes (sphere, disk, cylinder, core-shell, etc.) can
be determined from curve fitting for relatively narrow size distributions. The reliability of the method
of calculation for broader distributions depends on prior knowledge of the distribution.
This document assumes isotropically oriented nanoparticles of any shape in a test procedure. No
dimension of the nanoparticle shall be larger than defined by the scattering accessible to the specific
SAXS instrument. This generally limits the largest measurable particle size of the conventional
technique to 100 nm, although this limit can be significantly extended in samples with a very narrow
size distribution.
Small-angle neutron scattering is not described in this document but can be used without restriction
because the theory and application are similar.
A list of suitable references for further reading is given in the Bibliography.
© ISO 2020 – All rights reserved v

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 17867:2020(E)
Particle size analysis — Small angle X-ray scattering (SAXS)
1 Scope
This document specifies a method for the application of small-angle X-ray scattering (SAXS) to the
estimation of mean particle sizes in the 1 nm to 100 nm size range. It is applicable in dilute dispersions
where the interaction and scattering effects between the particles are negligible. This document
describes several data evaluation methods: the Guinier approximation, model-based data fitting, Monte-
Carlo–based data fitting, the indirect Fourier transform method and the expectation maximization
method. The most appropriate evaluation method is intended to be selected by the analyst and stated
clearly in the report. While the Guinier approximation only provides an estimate for the mean particle
diameter, the other methods also give insight in the particle size distribution.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 26824, Particle characterization of particulate systems — Vocabulary
ISO/TS 80004-2, Nanotechnologies — Vocabulary — Part 2: Nano-objects
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 26824, ISO/TS 80004-2 and
the following apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
3.1
particle
minute piece of matter with defined physical boundaries
Note 1 to entry: A physical boundary can also be described as an interface.
Note 2 to entry: A particle can move as a unit.
Note 3 to entry: This general particle definition applies to nano-objects.
[SOURCE: ISO 26824:2013, 1.1]
3.2
particle size
x
d
linear dimension of a particle determined by a specified measurement method and under specified
measurement conditions
Note 1 to entry: Different methods of analysis are based on the measurement of different physical properties.
Independent of the particle property actually measured, the particle size is reported as a linear dimension, e.g. as
the equivalent spherical diameter.
© ISO 2020 – All rights reserved 1

---------------------- Page: 6 ----------------------
ISO 17867:2020(E)

Note 2 to entry: Examples of size descriptors are those based at the opening of a sieve or a statistical diameter,
e.g. the Feret diameter, measured by image analysis.
Note 3 to entry: In ISO 9276-1:1998, the symbol x is used to denote the particle size. However, it is recognized that
the symbol d is also widely used to designate these values. Therefore the symbol x may be replaced by d.
3.3
radius of gyration
R
g
square root of the ratio of the moment of inertia to the particle mass
Note 1 to entry: Guinier radius (i.e. radius of gyration) is expressed in nanometres. Typical average radii are in
the range of 1 nm to 50 nm.
[SOURCE: ISO 26824:2013, 10.2]
4 Symbols
Symbol Description Unit
d Volume-squared-weighted mean particle diameter nm
vs
d Number-weighted mean particle diameter nm
num
g (r) Intensity-weighted particle size distribution
int
g (r) Number-weighted particle size distribution
num
g (r) Volume-weighted particle size distribution
vol
I Primary beam intensity with sample
out
I Primary beam intensity without sample
in
I(q) Scattered intensity (or scattering intensity)
M Number of degrees of freedom in fitting
N Number of particles
P(q, r) Particle form factor as functions of q-value and particle radius, r
Momentum transfer or q-value, magnitude of the scattering vector given by
−1
q nm
q = 4π/λ sin(θ)
−1
q Small angle resolution, minimum accessible q-value nm
min
−1
q Maximum accessible q-value nm
max
r Particle radius nm
R Radius of gyration (Guinier radius, see A.4) nm
g
t Optimum sample thickness mm
o
T Transmission
3
V Volume of particle nm
2θ Scattering angle deg or rad
λ Wavelength of the incident X-rays in vacuum nm
−1
μ Linear absorption coefficient mm
3
ρ(r) Electron density distribution nm
σ Standard deviation of size distribution nm
5 Principle of the method
When electromagnetic radiation passes through matter, a small fraction of the radiation may be
scattered due to electron density differences in the matter. The scattered radiation intensity profile (as
a function of the scattering angle or momentum transfer, q), contains information that can be used to
deduce morphological characteristics of the material. When X-rays are used to probe a geometrically
2 © ISO 2020 – All rights reserved

---------------------- Page: 7 ----------------------
ISO 17867:2020(E)

ordered group of particles or molecules (“crystals”), the well-known X-ray diffraction pattern is obtained
at wide scattering angles, which can be used to characterize the unit cell and lattice constants of such
crystalline material. In the small-angle regime (typically 2θ < 5 °; wavelength dependent), information
on the particle or pore dimensions within the material is available from the elastic scattering arising
from the electron density contrast between the particles and the medium in which they reside. This
is analogous to static light scattering and small-angle neutron scattering. A diagrammatic form of the
angular dependence of the X-ray scattered intensity of a titanium dioxide mixture (rutile and anatase)
is shown in Figure 1.
Key
X scattering angle 2θ (in degrees)
Y intensity
1 SAXS range
2 XRD range
Figure 1 — X-ray scattering diagram illustrating the small-angle SAXS region (left hand side) and
the wide-angle XRD (X-ray diffraction) region (right hand side) of a titanium dioxide powder
At low concentration, the small-angle scattering region contains information about the particle
morphology, which may be evaluated to extract either the particle size (distribution), or particle shape.
Only in very few cases is it possible to obtain both size and shape information. Different regions in
q are dominated by signals from a particular length range, and so can contain distinct (exploitable)
information aspects. In the low-q range, the Guinier approximation can be applied as an indicative
method to get an intensity weighted mean size, provided the particles are smaller than 2π/q . Model
min
fitting can be applied in the full range of q to compute a traceable particle size and size distribution
with associated uncertainties. Both methods can fail depending on data quality and particle properties.
At increased concentrations, i.e. those higher than typically one volume %, particle-particle interactions
and inter-particle interference can be relevant. Such interactions require sophisticated data modelling
and expert knowledge for data interpretation, which is beyond the scope of the present document.
In practice, a concentration ladder may be explored to determine the dependence of reported size on
concentration. If available, each sample shall be measured twice: in its original concentration, and
diluted 1:1 to allow identification of concentration artefacts. The result of both measurements shall be
arithmetically averaged and the uncertainty enhanced by the variation. If dilution is not possible for
technical reasons, this shall be stated in the report. In particular, the Guinier approximation is highly
sensitive to concentration-induced scattering effects.
6 Apparatus and procedure
A diagrammatic form of a SAXS instrument is shown in Figure 2.
© ISO 2020 – All rights reserved 3

---------------------- Page: 8 ----------------------
ISO 17867:2020(E)

Key
X 2θ or q
Y scattered intensity
1 X-ray source
2 optics
3 collimation system
4 sample
a
2θ.
Figure 2 — Diagrammatic form of a SAXS instrument, consisting of X-ray source, optics,
collimation system, sample holder, beam stop, and X-ray detector
The SAXS set-up consists of X-ray source, optics, collimation system, sample holder, beam stop,
and detector. In order to extract meaningful information from the measurement, the following key
parameters define the capability of the system:
— q-range: q and q ; number of sampled points in the Guinier region for Guinier approximation;
min max
— detector sensitivity and system background noise.
Most available X-ray sources produce divergent beams which shall be collimated for SAXS measurements.
With laboratory X-ray sources, multilayer optics are commonly used but basic SAXS measurements can
also be achieved with slit collimation. The X-ray flux on the sample is generally higher when optics is
used. Furthermore, multilayer coated optics can be used to generate a monochromatic X-ray beam.
The greatest challenge in SAXS is to separate the unscattered, transmitted beam (“direct beam”) from
the scattered radiation at small angles (around 0,1°). The direct beam is normally blocked by a beam
stop and parasitic scattering should be eliminated. The need for separation of primary and scattered
beam makes collimation of the primary beam mandatory.
There are two main options to collimate an X-ray beam (see Figure 3).
— Point collimation systems have multiple pinholes or crossed slits that limit the shape of the X-ray
beam to a low divergence and a small dimension (typically, the beam spot on the sample is less
than 0.8 mm in diameter). The scattering is normally centro-symmetrically distributed around
the primary X-ray beam. For isotropic samples, the scattering pattern in the detection plane
perpendicular to the X-ray beam exhibits circular contour lines around the point of incidence of the
primary beam. The illuminated sample volume is smaller than in line-collimation. Point collimation
allows the study of isotropic and anisotropic systems.
— Line-collimation instruments confine the beam in one dimension so that the beam profile is a long
and narrow line. The beam dimensions can be adapted to accommodate a given sample geometry.
Typical dimensions are 20 mm × 0,3 mm. The illuminated sample volume is larger compared to
point-collimation and the scattered intensity at the same flux density is proportionally larger. If
the system is isotropic, the resulting smearing can be reverted using a deconvolution procedure,
albeit at the cost of magnified uncertainties of the observed intensities. The investigation of
4 © ISO 2020 – All rights reserved

---------------------- Page: 9 ----------------------
ISO 17867:2020(E)

anisotropic nanostructure with such line-collimated instruments is not as straightforward as for
point collimation.
In addition, both the point and line collimation systems can use either a parallel or focused beam (see
Figure 4).
The scattered radiation (containing the morphological information, as described in Clause 5) forms a
pattern that contains the information on the size and structure of the sample. This pattern is detected
typically by a 1-dimensional or 2-dimensional flat X-ray detector situated behind the sample and
perpendicular to the direction of the primary beam. Some multipurpose diffractometers that combine
SAXS and diffraction use a scanning point (0-dimensional) detector. Detector classes commonly used
include photon-counting and integration type detectors, although in practice, the least problematic/
distorted measurements come from high-dynamic range, direct-detection, photon-counting detectors.
Key
1 X-ray source
2 collimation system
3 sample
Figure 3 — Point and line collimation types used in SAXS

© ISO 2020 – All rights reserved 5

---------------------- Page: 10 ----------------------
ISO 17867:2020(E)

a) Parallel beam
b) Point (2D) or line (1D) focused beam
Key
1 X-ray source
2 mirror
3 sample
Figure 4 — Focused and parallel beam set-up
7 Preliminary procedures and instrument set-up
Wavelength calibration (see Annex B) can be performed before conducting an experiment and thus
would be classified as a preliminary procedure, but this is only required for polychromatic sources.
If characteristic X-ray emission lines (e.g. copper Kα or molybdenum Kα lines) are used, a suitable
absorber can be used to check that the right emission line has been selected correctly (Nickel for Cu Kα,
Zirconium for Mo Kα). Utilization of a calibration material, such as silver behenate, should form part of
a full system qualification and fit-for-purpose specification as noted in Annex B.
Only if, in addition to the mean particle diameter and the particle size distribution, the (absolute)
concentration or volume fraction of scatterers is to be determined, the intensity shall be scaled to
absolute units. For this purpose, a variety of auxiliary calibration materials are available, including
water and glassy carbon. Alternatively, some instruments can determine this directly by means
of calibrated detectors, or measurement of the unattenuated primary beam intensity on the SAXS
detector. The use of semi-transparent beamstops to measure the beam intensity is not recommended
due to the radiation hardening effects of such, which can lead to inaccurate values.
All calibrations should be described in the analysis report.
8 Sample preparation
Sample preparation is simple and fast for SAXS measurements. The required sample volumes are small,
typically in a range of 5 μl to 50 μl for liquids and pastes, if copper radiation is used. Solid samples
2 2
require an area of (1 × 1) mm to (1 × 20) mm . The sample thickness is typically smaller than 1 mm and
can be tuned to optimize the scattering and limit the X-ray absorption, depending on the composition of
the sample.
Liquid samples are usually measured inside a thin-walled capillary, the diameter of which is typically
between 0,5 mm to 2 mm when the liquid primarily contains water or hydrocarbons. Solvents that
6 © ISO 2020 – All rights reserved

---------------------- Page: 11 ----------------------
ISO 17867:2020(E)

contain heavy atoms, for example, chlorine in chloroform, should be measured in smaller diameter
capillaries as the atoms strongly absorb the incident radiation, or higher energy radiation should be
used. Viscous samples can be measured better in a paste cell. It is strongly recommended to measure
liquid samples in a re-fillable or flow-through container, as this greatly reduces the risks of errors
encountered in the background subtraction procedure (incorrigible effects may lead to inaccurate
subtraction if non-identical sample containers are used for the two measurements).
Pastes, powders, and vacuum sensitive materials can be mounted into a sample holder with windows,
which shall be transparent to X-rays and exhibit little scattering themselves. Frequently used window
materials include polyimide films, mica or silicon nitride (see Reference [18]). Care should be taken
that the scattering from the window material does not affect the result of the measurement and can
be appropriately subtracted. For example, polyimide films exhibit a broad small-angle diffraction peak
−1
in the vicinity of q approximately 0,7 nm , which shall be correctly subtracted in the background
subtraction procedure.
Solids can be clamped onto frames with or without additional window foils for protection against the
vacuum. The sample thickness shall be chosen in line with the respective absorption of the material
(see Reference [17]). The optimum thickness, t , is given by
o
1
t = (1)
0
μ
where μ is the linear absorption coefficient of the material. The optimum specimen thickness
corresponds to a ratio of the primary beam intensity with an
...

Questions, Comments and Discussion