ISO 815-2:2019
(Main)Rubber, vulcanized or thermoplastic — Determination of compression set — Part 2: At low temperatures
Rubber, vulcanized or thermoplastic — Determination of compression set — Part 2: At low temperatures
This document specifies two methods for the determination of the compression set characteristics of vulcanized and thermoplastic rubbers at low temperatures. Method 1 derives from the methodology used in ISO 815-1. Method 2 uses a specified testing device, allowing to measure and record the test piece thickness during recovery. Due to the load applied during recovery in method 2, no correlation can be established between the results given by both methods. NOTE When rubber is held under compression, physical or chemical changes that prevent the rubber returning to its original dimensions after release of the deforming force can occur. The result is a set, where the magnitude of which depends on the time and temperature of compression as well as on the time, temperature, and conditions of recovery. At low temperatures, changes resulting from the effects of glass hardening or crystallization become predominant and, since these effects are reversed by raising the temperature, therefore, the measurements are always taken at the test temperature.
Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation rémanente après compression — Partie 2: À basses températures
Le présent document spécifie deux méthodes pour la détermination des caractéristiques de déformation rémanente après compression des caoutchoucs vulcanisés et thermoplastiques à températures basses. La méthode 1 découle de la méthodologie utilisée dans l'ISO 815-1. La méthode 2 utilise un dispositif d'essai spécifié permettant de mesurer et d'enregistrer l'épaisseur de l'éprouvette lors de la reprise élastique. En raison de la charge appliquée lors de la reprise élastique dans la méthode 2, aucune corrélation ne peut être établie entre les résultats donnés par les deux méthodes. NOTE Lorsqu'un caoutchouc est maintenu sous compression, des changements physiques ou chimiques peuvent se produire qui font que le caoutchouc, une fois relâché, ne recouvrera pas ses dimensions initiales. Il en résulte une déformation rémanente dont l'importance dépend à la fois de la durée et de la température de la compression ainsi que de la durée, de la température et des conditions de la reprise élastique. A basses températures, les changements consécutifs aux effets de la transition vitreuse ou de la cristallisation deviennent prédominants, et sachant que ces effets sont inversés par une élévation de la température, par conséquent, les mesurages sont toujours effectués à la température d'essai.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 815-2
Third edition
2019-11
Rubber, vulcanized or
thermoplastic — Determination of
compression set —
Part 2:
At low temperatures
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
déformation rémanente après compression —
Partie 2: À basses températures
Reference number
ISO 815-2:2019(E)
©
ISO 2019
---------------------- Page: 1 ----------------------
ISO 815-2:2019(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 815-2:2019(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
4.1 Method 1. 2
4.2 Method 2. 2
5 Apparatus for low temperature tests . 2
5.1 Method 1. 2
5.2 Method 2. 5
6 Calibration . 8
7 Test pieces . 8
7.1 Dimensions . 8
7.2 Preparation . 9
7.3 Number of test pieces . 9
7.4 Time interval between production and testing . 9
7.5 Conditioning .
...
NORME ISO
INTERNATIONALE 815-2
Troisième édition
2019-11
Caoutchouc vulcanisé ou
thermoplastique — Détermination
de la déformation rémanente après
compression —
Partie 2:
À basses températures
Rubber, vulcanized or thermoplastic — Determination of
compression set —
Part 2: At low temperatures
Numéro de référence
ISO 815-2:2019(F)
©
ISO 2019
---------------------- Page: 1 ----------------------
ISO 815-2:2019(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 815-2:2019(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
4.1 Méthode 1 . 2
4.2 Méthode 2 . 2
5 Appareillage pour les essais à basse température . 2
5.1 Méthode 1 . 2
5.2 Méthode 2 . 5
6 Étalonnage . 8
7 Éprouvettes . 8
7.1 Dimensions . 8
7.2 Préparation . 9
7.3 Nombre . 9
7.4 Délai entre la production et l'essai . 9
7.5 Conditionnement .
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.